Electron microscopy and electron diffraction study of crystallization of metastabel phases in amorphous FeB alloys
Abstract
Crystallization is investigated of amorphous Fe100–xBx where x = 14, 16, 18, 20 at% alloys using electron microscopy and electron diffraction. Above the eutectical composition, the crystallization in the alloys begins with the tetragonal metastable Fe3B and the ordered cubic Fe4B phases. Below the eutectical composition besides the Fe3B phase an orthorhombic supersaturated solid solution α-Fess with an order—disorder arrangement of B-atoms is formed. Both instable supersaturated solid solution (α-Fe)ss, Fe4B, and tetragonal, Fe3B contain similar short range order arrangement of FeB atoms in the form of bridging group. Die Kristallisation von amorphen Fe100–xBcx (x = 16; 16; 18; 20 At%)-Leigerungen wird mittels Elektronenmikroskopie und Elektronenbeugung untersucht. Die Kristallisation in Legierungen oberhalb der eutektischen Zusammensetzung beginnt mit tetragonalem metastabilen Fe3B und der geordneten kubischen Fe4B-Phase. Unterhalb der eutektischen Zusammensetzung bildet sich neben der Fe3B-Phase eine rhombische übersättigte Lösung, α-Fess, mit einer Ordnung—Unordnungsanordnung der B-Atome. Sowohl die instabile übersättigte Festkörperlösung (α-Fe)ss, Fe4B als auch die tetragonale Fe3B enthalten ähnliche Nahordnungsanordnungen der FeB-Atome in Form der brückenbildenden Gruppen.