Sol-Gel Synthesis, Structure, and Adsorption Properties of LiMgxMn(2 – x)O4 (0 ≤ x ≤ 0.7) Oxides
Аннотация
Lithium manganese oxides with a spinel structure LiMgxMn(2 – x)O4 doped with Mg2+ ions in the range 0 ≤ x ≤ 0.7, were obtained by sol-gel synthesis. Phase composition and morphology of obtained oxides were studied by X-ray powder diffraction and scanning electron microscopy. It is shown, that in the studied range 0 ≤ x ≤ 0.7 Mg-doped lithium manganese oxides saved the structure of the original cubic spinel LiMn2O4, while an increase in parameter a was observed from 8.175 to 8.309 Å and average crystallite size practically unchanged (30–36 nm). Samples of the initial LiMn2O4 spinel and Mg-doped spinel consisted of prismatic particles of submicron (0.1–0.2 µm) and micron (1.0–3.0 µm) sizes, respectively. The effect of the adsorbent dose (0.05–0.3 g/L) and pH (3.0–13.0) of the solution on the adsorption efficiency was studied. The adsorption isotherms of samples LiMg0.3Mn1.7O4 were described by the Langmuir monomolecular adsorption equation. An increase in the temperature of the model solution from 25 to 45°C was accompanied by an increase in the maximum adsorption of the LiMg0.3Mn1.7O4 samples from 10.50 to 10.98 mmol/g, which indicates the endothermic nature of the adsorption process. The kinetics of adsorption was well described by a pseudo-second order equation, which indicates the occurrence of chemical interaction during the adsorption process.