Transition‐Metal (Fe, Co, Ni) Based Metal‐Organic Frameworks for Electrochemical Energy Storage
Shasha ZhengSchool of Chemistry and Chemical Engineering Yangzhou University Yangzhou 225009 Jiangsu P. R. ChinaXinran LiSchool of Chemistry and Chemical Engineering Yangzhou University Yangzhou 225009 Jiangsu P. R. ChinaBingyi YanSchool of Chemistry and Chemical Engineering Yangzhou University Yangzhou 225009 Jiangsu P. R. ChinaQin HuSchool of Chemistry and Chemical Engineering Yangzhou University Yangzhou 225009 Jiangsu P. R. ChinaYuxia XuSchool of Chemistry and Chemical Engineering Yangzhou University Yangzhou 225009 Jiangsu P. R. ChinaXiao XiaoSchool of Chemistry and Chemical Engineering Yangzhou University Yangzhou 225009 Jiangsu P. R. ChinaHuaiguo XueSchool of Chemistry and Chemical Engineering Yangzhou University Yangzhou 225009 Jiangsu P. R. ChinaHuan PangSchool of Chemistry and Chemical Engineering Yangzhou University Yangzhou 225009 Jiangsu P. R. China
2017en
ABI
Аннотация
Transition‐metal (Fe, Co, Ni) based metal‐organic framework materials with controllable structures, large surface areas and adjustable pore sizes have attracted wide research interest for use in next‐generation electrochemical energy‐storage devices. This review introduces the synthesis of transition‐metal (Fe, Co, Ni) based metal‐organic frameworks and their derivatives with the focus on their application in supercapacitors and batteries.
Перевод пока недоступен
Идентификаторы
Цитирования и источники
Цитирований: 2Использованных источников: 0