Oxidation Behavior of <scp>MAX</scp> Phase <scp> <scp>Ti</scp> </scp> ₂ <scp> <scp>Al</scp> </scp> _{(1− <i>x</i> )} <scp> <scp>Sn</scp> </scp> _<i>x</i> <scp> <scp>C</scp> </scp> Solid Solution

MAX phase Ti 2 Al (1− x ) Sn x C solid solution with x = 0, 0.32, 0.57, 0.82, and 1 was synthesized by pressureless sintering of uniaxially pressed Ti , Al , Sn , and TiC powder mixtures. Annealing in air atmosphere at 200°C–1000°C triggered a sequence of oxidation reactions which reveal a distinct influence of solid solution composition on the oxidation process. With decreasing Al / Sn ratio, the characteristic temperature of accelerated oxidation reaction of A‐element was reduced from 900°C ( x = 0) to 460°C ( x = 1). SnO 2 was formed at temperatures significantly lower than TiO 2 (rutile) and Al 2 O 3 . Substitution of A‐element in MAX phase solid solution by low‐melting elements such as Sn may offer potential for reducing oxidation‐induced crack healing temperatures.