Synthesis of MAX Phases in the Zr-Ti-Al-C System
Bensu TuncaKU Leuven, Department
of Materials Engineering, Kasteelpark Arenberg 44, B-3001 Leuven, BelgiumThomas LapauwKU Leuven, Department
of Materials Engineering, Kasteelpark Arenberg 44, B-3001 Leuven, BelgiumOlesia M. KarakulinaUniversity of Antwerp, Department of Physics, Electron Microscopy for Materials
Science (EMAT), Groenenborgerlaan 171, B-2020 Antwerp, BelgiumMaria BatukUniversity of Antwerp, Department of Physics, Electron Microscopy for Materials
Science (EMAT), Groenenborgerlaan 171, B-2020 Antwerp, BelgiumThierry Cabioc’hInstitut Pprime, UPR 3346, CNRS-Université de Poitiers-ENSMA, SP2MI, Téléport 2-BP 30179, 86962 Futuroscope Chasseneuil
Cedex, FranceJoke HadermannUniversity of Antwerp, Department of Physics, Electron Microscopy for Materials
Science (EMAT), Groenenborgerlaan 171, B-2020 Antwerp, BelgiumRémi DelvilleSCK•CEN, Boeretang
200, B2400 Mol, BelgiumKonstantina LambrinouSCK•CEN, Boeretang
200, B2400 Mol, BelgiumJef VleugelsKU Leuven, Department
of Materials Engineering, Kasteelpark Arenberg 44, B-3001 Leuven, Belgium
2017en
ABI
Аннотация
X octahedral layers. The same ordering was also observed in 413 stackings present within the 312 phase. The decomposition of the secondary (Zr,Ti)C phase was attributed to the miscibility gap in the ZrC-TiC system.