Structural Elucidation, Electronic and Microwave Dielectric Properties of Ca(Sn<sub><i>x</i></sub>Ti<sub>1–<i>x</i></sub>)O<sub>3</sub>, (0 ≤ <i>x</i> ≤ 0.8) Lead-Free Ceramics
Abid ZamanDepartment of Physics, Riphah International University, Islamabad 44000, PakistanSarir UddinNasir MehboobDepartment of Physics, Riphah International University, Islamabad 44000, PakistanVineet TirthMechanical Engineering Department, College of Engineering, King Khalid University, Abha, Asir 61421, Kingdom of Saudi ArabiaAli AlgahtaniMechanical Engineering Department, College of Engineering, King Khalid University, Abha, Asir 61421, Kingdom of Saudi ArabiaMujahid AbbasFaculty of Materials and Manufacturing, Beijing University of Technology, Beijing 100124, ChinaMuhammad MushtaqFaculty of Materials and Manufacturing, Beijing University of Technology, Beijing 100124, ChinaAsad AliDepartment of Physics, Riphah International University, Islamabad 44000, PakistanFozia SultanaDepartment of Chemistry, University of science and technology China, Hefei, Anhui 230026, P.R.ChinaKhaled AlthubeitiDepartment of Chemistry, College of Science, Taif University, P.O. Box 11099, Taif 21944, Saudi ArabiaKamran UllahDepartment of Physics, Hazara University, Mansehra 21300, PakistanKhalid BashirDepartment of Physics, Riphah International University, Islamabad 44000, PakistanRafi UllahFaculty of Materials and Manufacturing, Beijing University of Technology, Beijing 100124, China
2022en
ABI
Аннотация
ions was analyzed in AC conductivity. The changes of dielectric properties such as complex permittivity, modulus spectroscopy, and dielectric loss at room temperature with a different frequency range of 1.00-2.00 GHz are discussed.
Перевод пока недоступен
Идентификаторы
Цитирования и источники
Цитирований: 5Использованных источников: 0