Optical Properties of LiNbO<sub>3</sub> Implanted with Ag<sup>+</sup> Ions
Shang DeyingFaculty of Engineering, Yamanashi University, 4-3-11 Takeda, Kofu 400Yukinori SaitoFaculty of Engineering, Yamanashi University, 4-3-11 Takeda, Kofu 400Shinji SuganomataFaculty of Engineering, Yamanashi University, 4-3-11 Takeda, Kofu 400
1994en
ABI
Аннотация
Ag + ions were implanted into LiNbO 3 held at room temperatures with the energy of 25 keV in the range of 2×10 15 to 8×10 16 ions/cm 2 . Absorption in the visible range was measured. LiNbO 3 implanted with Ag + ions shows brilliant reddish-violet and a large absorption peak at about 520 nm. Ag atoms aggregate during implantation and form very small flat particles of the size of about 0.3 to a few micrometers in surface layers of depths up to 16 nm.