Structure, phase composition, and strengthening of cast Al–Ca–Mg–Sc alloys
Н. А. БеловDepartment of Casting Process Technologies, National University of Science and Technology MISiS, Leninsky pr. 4, Moscow, 119049, RussiaЕ. А. НаумоваDepartment of Materials Science, Bauman Moscow State Technical University, ul. Vtoraya Baumanskaya 5, Moscow, 105005, RussiaT. A. BazlovaDepartment of Casting Process Technologies, National University of Science and Technology MISiS, Leninsky pr. 4, Moscow, 119049, RussiaЕ. В. АлексееваDepartment of Casting Process Technologies, National University of Science and Technology MISiS, Leninsky pr. 4, Moscow, 119049, Russia
2016en
ABI
Аннотация
The structure and phase composition of Al–Ca–Mg–Sc alloys containing 0.3 wt % Sc, up to 10 wt % Ca, and up to 10 wt % Mg have been investigated in the cast state and state after heat treatment. It has been shown that only binary phases Al4Ca, Al3Sc, and Al3Mg2 can be in equilibrium with the aluminum solid solution. It has been found that the maximum strengthening effect caused by the precipitation of Al3Sc nanoparticles for all investigated alloys is attained after annealing at 300–350°C.
Перевод пока недоступен
Идентификаторы
Цитирования и источники
Цитирований: 4Использованных источников: 0