Minimization of Internal Shrinkage Defects in Cast Parts Using 5VA Powder Solder Application

The article presents a method for eliminating the crystallization of thermal nodes and shrinkage defects in the form of micro-friable cavities. The method of soldering on castings from steel grades VNL-1 and VNL-6 using 5VA powder solder has been investigated. Also, the optimal soldering modes were determined, the effects of soldering modes on the properties of the base material and the soldered joint were studied, the corrosion resistance was investigated, the corrosion resistance of the soldered joints in corrosive environments. The conducted studies of sealing by soldering cast parts with microdefects lead to the following results: increased corrosion resistance; ensuring increased tightness; improving the presentation; elimination of surface microdefects.