Change of the Flow Stress at the Superconducting Transition in Lead—Indium Alloys

The change is studied of the flow stress (Δσ) induced by the superconducting transition in polycrystalline lead–indium alloys in a wide range of In concentrations (up to 50 at%) combined with magnetic induction control. Magnetic flux trapping is investigated as a function of the strain and concentration. The maximum flux trapping is observed in alloys containing about 2 at% In, i.e. in the vicinity of the type I to type II superconductivity transition in the Pb–In system. Allowance for magnetic flux trapping results in true strain and impurity concentration dependences of Δσ. For all the concentrations covered, Δσ weakly depends on the strain. The earlier observed minimum in the low In concentration range (near 2 at%) is entirely due to magnetic flux trapping. The now obtained results are discussed in terms of the current theories of the plasticity change at the superconducting transition. Es werden die durch den Suparleitungsübergang in polykristallinen Blei–Indium-Legierungen mit einem weiten Bereich der In-Konzentrationen (bis zu 50 At%) induzierten Änderungen der Fließspannung (Δσ) in Kombination mit der magnetischen Induktion untersucht. Das Anhaften des Magnetflusses wird in Abhängigkeit von der Spannung und Konzentration untersucht. Maximales Flußanhaften wird in Legierungen mit etwa 2 At% In d. h. in der Nähe des Supraleitungsübergangs Typ I zu Typ II im Pb–In-System beobachtet. Die Berücksichtigung des Magnetflußanhaftens führt zu einer echten Spannungs- und Störstellenkonzentrationsabhängigkeit von Δσ. Für alle untersuchten Konzentrationen hängt Δσ schwach von der Spannung ab. Das früher beobachtete Minimum im Bereich geringer In-Konzentrationen (bei etwa 2 At%) rührt vollständig vom Magnetflußanhaften her. Die nunmehr vorliegenden Ergebnisse werden mit den vorhanden Theorien der Plastizitätsänderung am Supraleitungsübergang diskutiert.

Перевод пока недоступен