Influence of a Nb interlayer on the oxidation behavior of a Cr coating deposited on Inconel 718 alloy substrate

Jialin DuJiangsu Key Laboratory of New Energy Devices & Interface Science, School of Chemistry and Materials Science, Nanjing University of Information Science & Technology, Nanjing, 210044, ChinaJun HuangJiangsu Key Laboratory of New Energy Devices & Interface Science, School of Chemistry and Materials Science, Nanjing University of Information Science & Technology, Nanjing, 210044, ChinaChao DongSchool of Materials Science and Engineering, Nanchang Hangkong University, Nanchang, 330063, ChinaShiyu CuiJiangsu Key Laboratory of New Energy Devices & Interface Science, School of Chemistry and Materials Science, Nanjing University of Information Science & Technology, Nanjing, 210044, ChinaWenjing LiuJiangsu Key Laboratory of New Energy Devices & Interface Science, School of Chemistry and Materials Science, Nanjing University of Information Science & Technology, Nanjing, 210044, ChinaXinhua ZhangJiangsu Key Laboratory of New Energy Devices & Interface Science, School of Chemistry and Materials Science, Nanjing University of Information Science & Technology, Nanjing, 210044, ChinaXingyue ZhuSchool of Materials Science and Engineering, Nanchang Hangkong University, Nanchang, 330063, ChinaJunming LuoSchool of Materials Science and Engineering, Nanchang Hangkong University, Nanchang, 330063, ChinaJianping ZhangJiangsu Key Laboratory of New Energy Devices & Interface Science, School of Chemistry and Materials Science, Nanjing University of Information Science & Technology, Nanjing, 210044, ChinaFan JiangJiangsu Key Laboratory of New Energy Devices & Interface Science, School of Chemistry and Materials Science, Nanjing University of Information Science & Technology, Nanjing, 210044, ChinaHaizhong ZhengSchool of Materials Science and Engineering, Nanchang Hangkong University, Nanchang, 330063, China

2025en

ABI

Аннотация

In order to improve the high-temperature oxidation resistance of Inconel 718 alloy, a Nb/Cr composite coating was manufactured using double glow plasma surface alloying (DGPSA). The addition of the Nb interlayer did not alter the phase composition of the Cr coating, which retained its bcc-Cr structure. However, it induced a shift in the preferred orientation of the Cr coating from (200) to (110). After 100-h cyclic oxidation at 800 °C and 900 °C, compared to the single Cr coating, the Nb/Cr composite coating formed a denser surface oxide layer with a reduced thickness. The total weight gain per unit area of the Inconel 718/Cr coated sample after oxidation for 100 h at 800 °C and 900 °C was 0.4707 mg/cm 2 and 0.6452 mg/cm 2 respectively; the Nb/Cr composite layer sample had weight gains of 0.2083 mg/cm 2 and 0.3700 mg/cm 2 after oxidation for 100 h at 800 °C and 900 °C respectively. When the temperature increases from 800 °C to 900 °C, Nb diffuses toward the Cr coating during the oxidation process, resulting in oxidative segregation. Meanwhile, Nb exerts a solute drag effect to inhibit the further supply of Cr to the surface layer, which induces a reduction in the size of oxide particles in the surface layer. Consequently, the material exhibits superior oxidation resistance.

Перевод пока недоступен

Идентификаторы

DOI: 10.1016/j.jmrt.2025.11.197

Цитирования и источники

Цитирований: 2Использованных источников: 0

Показатели — AkademScholar