Weak Localization in Polycrystalline Tin Dioxide Films

V.K. KsenevichFaculty of Physics, Belarusian State University, Nezalezhnastsi av.4, 220030 Minsk, BelarusV.A. DorosinetsFaculty of Physics, Belarusian State University, Nezalezhnastsi av.4, 220030 Minsk, BelarusDzmitry AdamchukFaculty of Physics, Belarusian State University, Nezalezhnastsi av.4, 220030 Minsk, BelarusJ. MacutkevičCenter for Physical Science and Technology, Sauletekio av. 3, 01100 Vilnius, LithuaniaJ. BanysFaculty of Physics, Vilnius University, Sauletekio av. 9, 10222 Vilnius, Lithuania

2020en

ABI

Аннотация

The electrical and magnetotransport properties of nanocrystalline tin dioxide films were studied in the temperature range of 4–300 K and in magnetic fields up to 8 T. SnO2−δ films were fabricated by reactive direct current (DC) magnetron sputtering of a tin target with following 2 stage temperature annealing of synthesized samples. The nanocrystalline rutile structure of films was confirmed by X-ray diffraction analysis. The temperature dependences of the resistance R(T) and the negative magnetoresistance (MR) were explained within the frame of a model, taking into account quantum corrections to the classical Drude conductivity. Extracted from the R(T) and R(B) dependences electron dephasing length values indicate the 3D character of the weak localization (WL) in our samples.

Ҳали таржима қилинмаган

Идентификаторлар

DOI: 10.3390/ma13235415

Иқтибослар ва манбалар

2 та иқтибос0 та фойдаланилган манба

Кўрсаткичлар — AkademScholar