Realization of Evaporated Electrode-Based Intrinsically Stretchable Ternary Organic Solar Cells through Encapsulation Strategy

Zhenye WangAnalytical and Testing Center, College of Chemistry and Chemical Engineering, Neijiang Normal University, Neijiang 641112, People’s Republic of ChinaDi ZhangHuazhong University of Science and TechnologyLvpeng YangWuhan National Laboratory for Optoelectronics, Huazhong University of Science and Technology, Wuhan 430074, People’s Republic of ChinaMeichen XuHuazhong University of Science and TechnologyJunfeng LiuWuhan National Laboratory for Optoelectronics, Huazhong University of Science and Technology, Wuhan 430074, People’s Republic of ChinaZhi WangHuazhong University of Science and TechnologyYerun GaoWuhan National Laboratory for Optoelectronics, Huazhong University of Science and Technology, Wuhan 430074, People’s Republic of ChinaLiyuan ZhangAnalytical and Testing Center, College of Chemistry and Chemical Engineering, Neijiang Normal University, Neijiang 641112, People’s Republic of ChinaLianbin NiuCollege of Physics and Electronic Engineering, Chongqing Normal University, Chongqing 401331, People’s Republic of ChinaMing ShaoHuazhong University of Science and Technology

2024en

Ochiq kirish: yoʻq

ABI

Annotatsiya

The mechanical properties of organic solar cells are of great importance to ensure their application in wearable or stretchable electronics. Here, we introduce polymer acceptor (N2200) into the active layer blend, and realize intrinsically stretchable organic solar cells (is-OSCs) with evaporated electrode via encapsulation strategy. The incorporation of N2200 simultaneously enhances the mechanical stretchability and PCE of is-OSCs, attributed to the enhanced polymer chain entanglement, and N2200 can act as tie molecules to provide electric connection among small molecule domains. More importantly, encapsulating the evaporated electrode-based is-OSCs leads to significant improvement in its mechanical stretchability, with 80% PCE retention under a large strain of 20%, compared to <2.5% strain for the unencapsulated ones. Additionally, encapsulated is-OSCs retained 67% PCE after 1000 test cycles at a stretch strain of 15%, whereas unencapsulated devices can only retain 33% PCE after 200 test cycles under a small strain of 5%.

Hali tarjima qilinmagan

Identifikatorlar

DOI: 10.1021/acsmaterialslett.4c01548

Iqtiboslar va manbalar

2 ta iqtibos0 ta foydalanilgan manba