Polyacrylonitrile‐Coordinated Perovskite Solar Cell with Open‐Circuit Voltage Exceeding 1.23 V

Chen ChenQingdao Institute of Bioenergy and Bioprocess Technology Chinese Academy of Sciences Qingdao 266101 P. R. ChinaXiao WangQingdao Institute of Bioenergy and Bioprocess Technology, Chinese Academy of Sciences, Qingdao, 266101 P. R. ChinaZhipeng LiQingdao Institute of Bioenergy and Bioprocess Technology, Chinese Academy of Sciences, Qingdao, 266101 P. R. ChinaXiaofan DuQingdao Institute of Bioenergy and Bioprocess Technology, Chinese Academy of Sciences, Qingdao, 266101 P. R. ChinaZhipeng ShaoQingdao Institute of Bioenergy and Bioprocess Technology, Chinese Academy of Sciences, Qingdao, 266101 P. R. ChinaXiuhong SunQingdao Institute of Bioenergy and Bioprocess Technology, Chinese Academy of Sciences, Qingdao, 266101 P. R. ChinaDachang LiuQingdao Institute of Bioenergy and Bioprocess Technology Chinese Academy of Sciences Qingdao 266101 P. R. ChinaCaiyun GaoQingdao Institute of Bioenergy and Bioprocess Technology, Chinese Academy of Sciences, Qingdao, 266101 P. R. ChinaLianzheng HaoQingdao Institute of Bioenergy and Bioprocess Technology Chinese Academy of Sciences Qingdao 266101 P. R. ChinaQiangqiang ZhaoQingdao Institute of Bioenergy and Bioprocess Technology Chinese Academy of Sciences Qingdao 266101 P. R. ChinaBingqian ZhangQingdao Institute of Bioenergy and Bioprocess Technology Chinese Academy of Sciences Qingdao 266101 P. R. ChinaGuanglei CuiQingdao Institute of Bioenergy and Bioprocess Technology Chinese Academy of Sciences Qingdao 266101 P. R. ChinaShuping PangQingdao Institute of Bioenergy and Bioprocess Technology Chinese Academy of Sciences Qingdao 266101 P. R. China

2021en

ABI

Annotatsiya

In solution-processed organic-inorganic halide perovskite films, halide-anion related defects including halide vacancies and interstitial defects can easily form at the surfaces and grain boundaries. The uncoordinated lead cations produce defect levels within the band gap, and the excess iodides disturb the interfacial carrier transport. Thus these defects lead to severe nonradiative recombination, hysteresis, and large energy loss in the device. Herein, polyacrylonitrile (PAN) was introduced to passivate the uncoordinated lead cations in the perovskite films. The coordinating ability of cyano group was found to be stronger than that of the normally used carbonyl groups, and the strong coordination could reduce the I/Pb ratio at the film surface. With the PAN perovskite film, the device efficiency improved from 21.58 % to 23.71 % and the open-circuit voltage from 1.12 V to 1.23 V, the ion migration activation energy increased, and operational stability improved.

Hali tarjima qilinmagan

Identifikatorlar

DOI: 10.1002/anie.202113932

Iqtiboslar va manbalar

2 ta iqtibos0 ta foydalanilgan manba