Transferred hyperfine fields at the tin site in the heusler-type alloys Co2YSn (Y = Ti, Zr, Hf, V)

The hyperfine magnetic fields at the tin site in ferromagnetic Heusler type alloys Co2YSn (Y = Ti, Zr, Hf, V) were measured by the Mössbauer effect using 23.9 keV γ-line in 119mSn. The samples were checked by X-ray diffraction analysis, magnetization measurements, and neutron diffraction method (for Co2TiSn only). The results were interpreted in terms of the Blandin-Campbell formalism and qualitative agreement with the experimental data was obtained for a number of conduction electrons per atom of about 0.5. Mit dem Mößbauereffekt wurden die magnetischen Hyperfeinfelder an den Zinnplätzen der ferromagnetischen Heusler-Legierungen Co2YSn (Y = Ti, Zr, Hf, V) mittels der 23,9 keV γ-Linie von 119mSn gemessen. Die Proben wurden durch Röntgenstrahlenanalyse, Magnetisierungsmessungen und Neutronenbeugungsmethoden (nur für Co2TiSn) untersucht. Die Ergebnisse werden mit dem Blandin-Campbell-Formalismus interpretiert, wobei qualitative Übereinstimmung mit den experimentellen Werten für eine Anzahl von Leitungselektronen von etwa 0,5 pro Atom erhalten wird.

Hali tarjima qilinmagan