Intensity-dependent loss properties of window materials at 248 nm
P. ŠimonLaser-Laboratorium Göttingen e.V., Robert-Bosch-Breite 10, D-3400 Göttingen, Federal Republic of GermanyS. SzatmáriMax-Planck-Institut für biophysikalische Chemie, Abteilung Laserphysik, Postfach 28 41, D-3400 Göttingen, Federal Republic of GermanyH. GerhardtLaser-Laboratorium Göttingen e.V., Robert-Bosch-Breite 10, D-3400 Göttingen, Federal Republic of Germany
1989en
ABI
Annotatsiya
Transmission of fused silica, CaF(2), LiF, and MgF(2) is measured using 450-fsec, 248-nm pulses in the range 10-120 GW/cm(2). Different loss mechanisms such as scattering of transmitted radiation, color-center formation, and multiphoton absorption were studied separately. For fused silica a two-photon absorption mechanism is found, while for CaF(2), LiF, and MgF(2) three-photon absorption and absorption due to color-center formation are found as dominant absorption mechanisms.