Structure engineering in vacuum-arc-deposited coatings of the MoN–CrN system

В. М. БересневKarazin Kharkiv National University, 61022, Kharkiv, UkraineO. V. SоbоlNational Technical University Kharkiv Polytechnic Institute, 61002, Kharkiv, UkraineA.D. PogrebnjakSumy State University, 40007, Sumy, UkraineS. S. GrankinKarazin Kharkiv National University, 61022, Kharkiv, UkraineВ. А. СтолбовойNational Science Center Kharkiv Institute of Physics and Technology, 61108, Kharkiv, UkraineП. В. ТурбінKarazin Kharkiv National University, 61022, Kharkiv, UkraineА. А. МейлеховNational Technical University Kharkiv Polytechnic Institute, 61002, Kharkiv, UkraineMariia ArseenkoBelgorod National Research University, Belgorod, 308015, Russia

2016en

ABI

Annotatsiya

The possibilities of structure engineering in multilayer coatings of the MoN–CrN system with relatively low heats of formation of component transition metal nitrides are demonstrated by varying pressure P N of reactive gas (nitrogen) and negative bias voltage–U s applied to a metal substrate. It is established that, by changing P N from 7 × 10–4 to 3 × 10–3 Torr, it is possible to obtain coatings in two significantly different structural-phase states. A multilayer nonisostructural composite with hexagonal crystalline lattice in CrN layers and cubic type lattice in MoN layers is formed at low pressure, whereas an isostructural state with cubic lattice in both nitride layers is formed at high pressure. The existence of two types of structural states allows multilayer coatings with controlled hardness to be obtained, which reaches 38 GPa in the isostructural state.

Hali tarjima qilinmagan

Identifikatorlar

DOI: 10.1134/s1063785016050205

Iqtiboslar va manbalar

2 ta iqtibos0 ta foydalanilgan manba

Koʻrsatkichlar — AkademScholar