Mechanical activation and physical properties of Pb(Zr<sub>0.56</sub>Ti<sub>0.44</sub>)O<sub>3</sub>
Marina SirotaDon State Technical University, Rostov-on-Don, RussiaК. Г. АбдулвахидовSouthern Federal University, Rostov-on-Don, RussiaAndriy P. BudnykSouthern Federal University, Rostov-on-Don, RussiaА. В. СолдатовSouthern Federal University, Rostov-on-Don, RussiaAram L. BugaevSouthern Federal University, Rostov-on-Don, RussiaT. A. LastovinaSouthern Federal University, Rostov-on-Don, RussiaYu. V. KabirovSouthern Federal University, Rostov-on-Don, RussiaM. I. MazuritskiySouthern Federal University, Rostov-on-Don, RussiaPavel PlyakaSouthern Scientific Center of the Russian Academy of Sciences, Rostov-on-Don, RussiaS. N. KallaevInstitute of Physics, Dagestan Scientific Center, Russian Academy of Sciences, Makhachkala, RussiaЗ. М. ОмаровInstitute of Physics, Dagestan Scientific Center, Russian Academy of Sciences, Makhachkala, RussiaS. A. SadykovDagestan State University, Makhachkala, RussiaBashir AbdulvakhidovDagestan State University, Makhachkala, RussiaI. V. MardasovaDon State Technical University, Rostov-on-Don, RussiaM. A. VitchenkoDon State Technical University, Rostov-on-Don, Russia
2018en
ABI
Annotatsiya
The Pb(Zr0.56Ti0.44)O3 (PZT) ceramics was subjected to a pressure-induced activation at 320 MPa in a Bridgman anvil, where a load pressure was combined with a shear deformation. The induced changes in the linear and angular parameters of a unit cell, in the ratio of coexisting rhombohedral (R3m) and tetragonal (P4mm) phases as well as in the dielectric properties were analyzed.
Hali tarjima qilinmagan
Identifikatorlar
Iqtiboslar va manbalar
2 ta iqtibos0 ta foydalanilgan manba