Formation of the Spinel Phase in the Layered Composite Cathode Used in Li-Ion Batteries

Meng GuEnvironmental Molecular Science Laboratory, Pacific Northwest National Laboratory, 902 Battelle Boulevard, Richland, Washington 99352, USAIlias BelharouakChemical Sciences and Engineering Division, Argonne National Laboratory, 9700 South Cass Avenue, Argonne, Illinois 60439, United StatesJianming ZhengPacific Northwest National LaboratoryHuiming WuChemical Sciences and Engineering Division, Argonne National Laboratory, 9700 South Cass Avenue, Argonne, Illinois 60439, United StatesJie XiaoPacific Northwest National LaboratoryArda GençKhalil AmineChemical Sciences and Engineering Division, Argonne National Laboratory, 9700 South Cass Avenue, Argonne, Illinois 60439, United StatesSuntharampillai ThevuthasanEnvironmental Molecular Science LaboratoryDonald R. BaerEnvironmental Molecular Science LaboratoryJi‐Guang ZhangPacific Northwest National LaboratoryNigel D. BrowningJun LiuChongmin WangEnvironmental Molecular Science Laboratory
2012en
ABI

Annotatsiya

Pristine Li-rich layered cathodes, such as Li(1.2)Ni(0.2)Mn(0.6)O(2) and Li(1.2)Ni(0.1)Mn(0.525)Co(0.175)O(2), were identified to exist in two different structures: LiMO(2)R3[overline]m and Li(2)MO(3)C2/m phases. Upon 300 cycles of charge/discharge, both phases gradually transform to the spinel structure. The transition from LiMO(2)R3[overline]m to spinel is accomplished through the migration of transition metal ions to the Li site without breaking down the lattice, leading to the formation of mosaic structured spinel grains within the parent particle. In contrast, transition from Li(2)MO(3)C2/m to spinel involves removal of Li(+) and O(2-), which produces large lattice strain and leads to the breakdown of the parent lattice. The newly formed spinel grains show random orientation within the same particle. Cracks and pores were also noticed within some layered nanoparticles after cycling, which is believed to be the consequence of the lattice breakdown and vacancy condensation upon removal of lithium ions. The AlF(3)-coating can partially relieve the spinel formation in the layered structure during cycling, resulting in a slower capacity decay. However, the AlF(3)-coating on the layered structure cannot ultimately stop the spinel formation. The observation of structure transition characteristics discussed in this paper provides direct explanation for the observed gradual capacity loss and poor rate performance of the layered composite. It also provides clues about how to improve the materials structure in order to improve electrochemical performance.

Hali tarjima qilinmagan

Identifikatorlar

Iqtiboslar va manbalar

2 ta iqtibos0 ta foydalanilgan manba