Property of Radiation-Induced Defects in Germanium Single Crystals

To study the property of defects produced in high-purity and p-type germanium single crystals by thermal neutron, fast neutron or electron irradiation, annealing experiments on irradiated samples were performed with electrical measurements and a deep-level transient spectroscopy technique. The annealing behavior of defects produced by the recoil energy of ( n , γ) reaction in a high-purity sample irradiated with thermal neutrons indicates that interstitial arsenic atoms and interstitial gallium atoms are restored to lattice sites during annealing in the temperature range from 180° C to 240° C and that from 260° C to 340° C, respectively. The defects produced by neutron irradiation were annihilated by annealing for 20 min at 380° C. Two hole traps located at E v +0.32 eV and E v +0.53 eV were formed in a high-purity crystal by electron irradiation.