Maqola

Comprehensive stabilization mechanism of electron-beam irradiated polyacrylonitrile fibers to shorten the conventional thermal treatment

Sejoon ParkCarbon Convergence Materials Research Center, Institute of Advanced Composite Materials, Korea Institute of Science and Technology, 92, Chudong-ro, Bongdong-eup, Wanju-gun, Jeollabuk-do 565-905, Republic of KoreaSeung Hwa YooCarbon Convergence Materials Research Center, Institute of Advanced Composite Materials, Korea Institute of Science and Technology, 92, Chudong-ro, Bongdong-eup, Wanju-gun, Jeollabuk-do 565-905, Republic of KoreaHa Ri KangCarbon Convergence Materials Research Center, Institute of Advanced Composite Materials, Korea Institute of Science and Technology, 92, Chudong-ro, Bongdong-eup, Wanju-gun, Jeollabuk-do 565-905, Republic of KoreaSeong Mu JoCarbon Convergence Materials Research Center, Institute of Advanced Composite Materials, Korea Institute of Science and Technology, 92, Chudong-ro, Bongdong-eup, Wanju-gun, Jeollabuk-do 565-905, Republic of KoreaHan‐Ik JohCarbon Convergence Materials Research Center, Institute of Advanced Composite Materials, Korea Institute of Science and Technology, 92, Chudong-ro, Bongdong-eup, Wanju-gun, Jeollabuk-do 565-905, Republic of KoreaSungho LeeCarbon Convergence Materials Research Center, Institute of Advanced Composite Materials, Korea Institute of Science and Technology, 92, Chudong-ro, Bongdong-eup, Wanju-gun, Jeollabuk-do 565-905, Republic of Korea

2016en

ABI

Annotatsiya

An electron beam was irradiated on polyacrylonitrile (PAN) fibers prior to thermal stabilization. The electron-beam irradiation effectively shortened the thermal stabilization process by one fourth compared with the conventional thermal stabilization process. A comprehensive mechanistic study was conducted regarding this shortening of the thermal stabilization by electron-beam irradiation. Various species of chain radicals were produced in PAN fibers by electron-beam irradiation and existed for a relatively long duration, as observed by electron spin resonance spectroscopy. Subsequently, these radicals were gradually oxidized to peroxy radicals in the presence of oxygen under storage or heating. We found that these peroxy radicals (CO) enabled such an effective shortcut of thermal stabilization by acting as intermolecular cross-linking and partial aromatization points in the low temperature range (100-130 °C) and as earlier initiation seeds of successive cyclization reactions in the next temperature range (>130-140 °C) of thermal stabilization. Finally, even at a low irradiation dose (200 kGy), followed by a short heat treatment (230 °C for 30 min), the PAN fibers were sufficiently stabilized to produce carbon fibers with tensile strength and modulus of 2.3 and 216 GPa, respectively, after carbonization.

Hali tarjima qilinmagan

Identifikatorlar

DOI: 10.1038/srep27330

Iqtiboslar va manbalar

2 ta iqtibos0 ta foydalanilgan manba

Koʻrsatkichlar — AkademScholar