Mössbauer effect studies of ferrous oxides Fe1−xO

Mössbauer measurements were performed at room temperature for a group of nonstoichiometric iron oxides of the Fe1-xO type with 0.002≦x≦0.250. The measured spectra for the samples with x ranging from 0.002 to 0.083 represent quadrupole split Fe2+ doublets and an unseparated Fe3+ singlet. For the samples with x≧0.084 apart from asymmetric quadrupole splitting, a double Zeeman splitting appears, due to the formation ofmagnetite-like clusters. The intensity ratio of the quadrupole pattern of the wüstite phase to the Zeeman pattern of the magnetite phase decreases with increasing x to zero for x = 0.250 (pure synthetized magnetite), which is in agreement with X-ray diffraction analyses. Mößbaueruntersuchungen wurden bei Zimmertemperatur an einer Gruppe nichtstöchiometrischer Eisenoxide vom Fe1-xO-Typ mit 0,002≦x≦0,250 durchgeführt. Die gemessenen Spektren für Proben mit x zwischen 0,002 und 0,083 stellen durch Quadrupolwechselwirkung aufgespaltene Fe2+-Doubletts und ein nichtgetrenntes Fe3+-Singulett dar. Für Proben mit x≧0,084 tritt außer einer asymmetrischen Quadrupolaufspaltung eine doppelte Zeemanaufspaltung durch die Bildung von magnetitähnlichen Clustern auf. Das Intensitätsverhältnis des Quadrupoldiagramms der Wüstit-Phase zum Zeemandiagramm der Magnetit-Phase fällt in Übereinstimmung mit Röntgenstrahlbeugungs-analysen mit wachsendem x auf null ab für x = 0,250 (reines synthetisiertes Magnetit).

Ҳали таржима қилинмаган