DEVELOPMENT OF 280X29NL ALLOY LIQUEFACTION TECHNOLOGY TO INCREASE THE HARDNESS AND CORROSION RESISTANCE OF CAST PRODUCTS
Turaxodjaev NodirTashkent State Technical University, UzbekistanSaidmakhamadov NosirTashkent State Technical University, UzbekistanSaidkhodjaeva ShokhistaTashkent State Technical University, UzbekistanFurkat OdilovTashkent State Technical University, UzbekistanKholmirzaev NozimjonTashkent State Technical University, UzbekistanBekchanova ValidaTashkent State Technical University, UzbekistanN TurakhodjaevY WangS BekmirzaevN SaidmakhamadovUbaydullaevN SaidmaxamadovU XaydarovB EgamberdievT DjahongirovichS MuysinaliyevichT NodirTashkent State Technical University, UzbekistanT SherzodZ RuslanT SarvarB AzamatJ AndreyM YahyojonE UmarovU MardonovK AbdirakhmonovA EshkulovB RakhmatovS TursunbaevS TashbulatovM KuchkorovaU ErkinM UmidjonS UmidaM AkramovS TurakhujaevaA TurakhujaevaJ KamalovU Shoazimova
ABI
Аннотация
This article, by changing the chemical composition of high-chromium 280X29NL cast iron and processing its composition Ti from 0.93% to 1.78%, the elongation strength of highchromium cast iron increased and without affecting the hardness of the alloy, Ti addition was added. 'The structure was improved by swelling. The strength of the secondary carbides in the matrix also increased without loss of hardness. In addition, a new brand of alloy 280X29NL (sample 2), which is economically inexpensive and corrosive, was developed without compromising the mechanical properties of the alloy.
Мавзулар
Идентификаторлар
Иқтибослар ва манбалар
Кўрсаткичлар — AkademScholar · Тез орада