Preparation and Morphological Studies of Epitaxial Layers of a Solid Solution Si1–xGex

The article shows the selection of the optimal process regime for the growth of epitaxial layers of Si1–xGex solid solutions from tin and gallium solution – melt on a Si<111> substrate, with the lowest dislocation densities that we experimentally achieved. An exponential relationship was found between the values of the dislocation density and the film thickness.With a smooth variable composition of the structure, respectively, by smoothly changing the lattiece parameters of the graded-gap solid solution, structurally perfect epitaxial layers Si1–xGex (0 < x < 1) were obtained